Strenx® weathering steels
Show specs in Metric Imperial

General Product Description

The high-strength, corrosion resistant structural steel at 700 MPa.

Strenx® 700 HR W is a hot-rolled weathering steel made for cold forming, with a minimum yield strength of 700 MPa for stronger and lighter structures.

Strenx® 700 HR W meets or exceeds the requirements of S700MC in EN 10149-2. Typical applications include a wide range of components and parts

in demanding load-bearing structures. Strenx® 700 HR W comes in coils, slit coils or cut-to-length sheets.

Dimension Range

Strenx® 700 HR W is available in thicknesses of 3.0 - 6.1 mm and widths up to 1550 mm as coils, slit coils or cut to length sheets in lengths up to 13.6 m.

Mechanical Properties

Hide/Show specific columns Edit
Select columns to display
    Thickness
    (mmin)
    Yield strength ReH 1)
    (min MPaksi)
    Tensile strength Rm
    (MPaksi)
    Elongation A5
    (min %)
    Min. inner bending radius for a 90° bend 2)
    3.0 - 6.10.118 - 0.240 700101 750 - 950109 - 138 12 2 x t
    Compare parameters

    Select one parameter to compare

    Comparison

      The mechanical properties are tested in the longitudinal direction.

      1) If ReH is not applicable then Rp0.2 is used.

      2) For both longitudinal and transverse direction.

      Impact Properties

      Hide/Show specific columns Edit
      Select columns to display
        Product Min. impact energy for longitudinal testing,
        Charpy V 10x10 mm test specimen 1)
        Strenx® 700 HR W 40 J / -20 °C29 ft-lbs / -4 °F
        Compare parameters

        Select one parameter to compare

        Comparison

          Product
          Strenx® 700 HR W
          Min. impact energy for longitudinal testing,
          Charpy V 10x10 mm test specimen 1)
          40 J / -20 °C29 ft-lbs / -4 °F

          1) Impact testing according to EN ISO 148-1 is performed on thicknesses ≥ 5 mm. The specified minimum value corresponds to a full-size specimen.

          Chemical Composition (ladle analysis)

          Hide/Show specific columns Edit
          Select columns to display
            C
            (max %)
            Si
            (max %)
            Mn
            (max %)
            P
            (max %)
            S
            (max %)
            Cr
            (max %)
            Cu
            (max %)
            Ti
            (max %)
            0.12 0.60 2.10 0.015 0.010 1.25 0.50 0.15
            Compare parameters

            Select one parameter to compare

            Comparison

              The steel is grain refined.

              Carbon Equivalent CET(CEV)

              Hide/Show specific columns Edit
              Select columns to display
                Thickness (mmin) 3.0 - 6.10.118 - 0.240
                Typ CET(CEV) 0.26 (0.47)
                Compare parameters

                Select one parameter to compare

                Comparison

                  Thickness (mmin)
                  Typ CET(CEV)
                  3.0 - 6.10.118 - 0.240
                  0.26 (0.47)
                  CET and CEV formula

                  Tolerances

                  More details are given in SSAB’s brochure Strenx® Guarantees.

                  Thickness

                  Tolerances according to Strenx® Thickness Guarantee.

                  Strenx® Guarantees offer considerably narrower thickness tolerances compared to EN 10051. 

                  Length and Width

                  Width and length tolerances according to SSAB standard.

                  SSAB standard offer narrower width and length tolerances compared to EN 10051.

                  Length tolerances only apply for cut to length sheets.

                  Shape

                  Tolerances according to EN 10051. Narrower tolerances according to the SSAB standard are available on request.

                  Surface Properties

                  According to EN 10163-2 Class A, Subclass 3.

                  Delivery Conditions

                  Thermomechanically Rolled. Strenx® 700 HR W is available in as rolled or pickled surface condition with mill or cut edge.

                  Delivery requirements can be found in SSAB’s brochure Strenx® Guarantees or www.ssab.com.

                  Fabrication and Other Recommendations

                  Welding, bending and machining

                  Strenx® 700 HR W has good welding, cold forming and cutting performance.

                  Strenx® 700 HR W is not suited for heat treatments at temperatures above 580°C since the material then may lose its guaranteed properties. 

                  The weldability of Strenx® 700 HR W is good. All the conventional fusion welding methods can be used. To obtain the same corrosion resistance in the weld as in the base metal, special filler metals should be used. Painting of Strenx® weather resistant steel is easy and will result in good paint adhesion. This can further increase the maintenance interval of the component. In order to ensure the uniform colour of the patina, all impurities must be cleaned from the steel surface. Organic impurities such as oil or protective greases must be removed by washing with suitable solvent.

                  Surface oxidation, oxides or rust can be removed by either shot-blasting or pickling. This will also accelerate the patina formation process. Shot-blasting is not recommended for thicknesses below 4 mm. The surface of a clean weathering steel surface can be pre-patinated by allowing the surface to get wet and dryin repeated intervals.

                  For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support.

                  Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the products.

                  Ready to upgrade?

                  Upgrading from Strenx® 700 W to Strenx® 960 W means you can improve the performance and reduce the weight of your equipment. The increase in yield strength by 37% allows for a great leap in the equipment’s load-bearing capacity. Get in touch with our steel specialists at SSAB Tech Support or SSAB Knowledge Service Center for an update on upgrading.